Technical Details for PA6 Chips, A-Grade, Relative Viscosity 2.70
- Appearance and color: Natural white
- Size of chips: 2-4mm
- Humidity fraction by mass, no more than: 0.80%
- Relative viscosity, within the limits: 2.70 +/- 0.05
- Fraction of extractive substances by mass, no more than: 0.80%
- Fraction of not cut through chips by mass, no more than: 0.50%
- Melting temperature no less than: 215°c
Technical details for nylon-6 glas fiber reinforced chips PA-SV-30
Index Name |
Meaning of the normalized indexes |
PA-SV-30 |
| TC 6-13-00204027-142-2004
|
External |
Granules of the same color (according to sample) |
Mass content of granules size 2-5mm, % not less |
97 |
Mass content of the stuff, % |
30+/-3 |
Transverse stress at break, Mpa, not less |
200 |
Tensile strength at yield, Mpa, not less |
155 |
Tensile strain at break,%, not less |
3 |
Flexural modulus, GPa |
7 +/-1 |
Moulding shrinkage parallel, % |
0,5 ÷ 0,8 |
Water absorption, %, not more than |
0,2 |
Glass Fibre
| Property |
method |
method |
unit |
tolerances |
| moisture content |
- |
- |
% |
<0.10 |
| Filament diameter |
- |
- |
|
10 |
| Fibre length |
- |
- |
mm |
3-4.5 |
| Binder content (range) |
ISO1887 |
AV-0201 |
% |
0.5-1.30 |
Technical Details for PA6 Chips, A-Grade, Relative Viscosity 2.45
- Appearance and color: Natural white
- Size of chips: 2-4mm
- Humidity fraction by mass, no more than: 0.06%
- Relative viscosity, within the limits: 2.45 +/- 0.05
- Fraction of extractive substances by mass, no more than: 0.80%
- Fraction of not cut through chips by mass, no more than: 0.50%
- Melting temperature no less than: 215°c
Technical Details for PA6 Chips, A-Grade, Relative Viscosity 3.20
- Appearance and color: Natural white
- Size of chips: 2-4mm
- Humidity fraction by mass, no more than: 0.6%
- Relative viscosity, within the limits: 3.20 +/- 0.05
- Fraction of extractive substances by mass, no more than: 0.80%
- Fraction of not cut through chips by mass, no more than: 0.50%
- Melting temperature no less than: 215°c
|
|